Fluoroelastomer FKM Premixed Rubber Compound Fluorine Rubber Viton for High and Low Temperature Sealing Perfluoroelastomer Ffkm Rubber Compound Peroxide Comp

Date：2023-09-20 09:50:50VIew：

Description: FKM premixed rubber is a kind of fluororubber premixed rubber added with a small amount of processing aids, fillers and all additive of curing systems. It solves the problem that the fluororubber vulcanizing agent is difficult to disperse during processing, and greatly improves the mixing efficiency of fluororubber.
Special properties:
Excellent wear & tear resistance; excellent ozone resistance & weather resistance
Heat resistance comparable to silicone rubber, better than any other rubber; excellent
resistance to superheated water or water vapor, excellent high vacuum resistance Good
appearance.
Excellent corrosion resistance, excellent resistance to moderate doses of radiation
Good low temperature performance
Good storage stability
Excellent antistatic property in low frequency and low voltage occasions
Calendering, extrusion fast, smooth surface, high strength, high hardness & low pressure
deformation, high chemical stability

Main applications:
FKM premixed adhesives are mainly used in high and low temperature sealing, vacuum equipment, chemical equipment, automobiles, aviation and other fields. It is also one of the indispensable high-performance materials for cutting-edge science and technology such as modern aviation, missiles, rockets, space navigation, ships, and atomic energy.

Characteristics:
Type ...............................................................................FKM
Natural color...................................................................... translucent
Relative density, g/cm3....................................................... 1.85-1.95
Fluorine content.................................................................... 60±5%
Moisture content, %...............................................................≤0.1
ML 1+4@100ºC..............................................................40± 5
Volatile content................................................................... <1.0%
Color ....................................................................................White

Curing Condition: (1) 1st vulcanization at 175 ºC × 10min
(2) 2nd vulcanization at 230ºC× 16h

Reference recipe :(phr)

FKM premixed rubber	100
N990	30
MgO	3
Ca(OH)₂	6
WS280	1
Palm wax	1

Product performance:

product name			LXF100CA	LXF200CA
Project	Test Methods	unit	Typical value
Mooney viscosity(ML 1+4@100ºC)			53	48
Vulcanization performance test:180ºC×5min×1arc
Minimum torque	ASTM D2048	lb-in	0.40	0.38
Maximum torque		lb-in	9.02	8.46
Scorch Time TS2		s	72	73
Positive vulcanization time TC90		s	140	136
1,Mechanical properties 1.1 First vulcanization: 175ºC×10min, Second vulcanization: 230ºC×16h
Proportion	ASTM D297	g/cm3	1.938	1.936
Hardness (Shore A)	ASTM D2240	Points	70	70
Tear strength	ASTM D412	MPa	11.28	10.58
Elongation at break		%	257	248
M100		MPa	5.45	5.40
1, Mechanical properties 1.2 Changes in properties after aging at 200°C for 504 hours
Hardness (Shore A) change	ASTM D2240	Points	+3	+5
Change in breaking strength	ASTM D412	%	-4.2	-8.0
Elongation at break change	ASTM D412	%	-15.5	-22.5
2,Oil resistance 2.1 Changes in resistance to FAM B oil at 23°C for 48 hours
Hardness (Shore A) change	ASTM D2240	Points	-6	-10
Volume change rate change	ASTM D471	%	+10.5	+16.5
2,Oil resistance 2.2 Performance after aging and drying at 100°C for 48 hours after being resistant to FAM B oil at 23°C for 48 hours
Hardness (Shore A)	ASTM D2240	Points	70	70
Tear strength	ASTM D412	%	10.28	9.98
Elongation at break	ASTM D412	%	245	224
volume change rate	ASTM D471	%	+0.23	+0.52
2,Oil resistance 2.3 Diesel resistance change at 23°C for 48 hours
Hardness (Shore A) change	ASTM D2240	Points	0	-3
volume change rate	ASTM D471	%	-0.03	+3.98
2,Oil resistance 2.4 Performance after aging at 23°C for 48 hours against diesel oil and drying at 100°C for 48 hours
Hardness (Shore A)	ASTM D2240	Points	70	69
Tear strength	ASTM D412	%	10.25	9.67
Elongation at break	ASTM D412	%	238	228
Volume change rate%	ASTM D471	%	+0.34	+0.92
2,Oil resistance 2.5 Biodiesel resistance (RME) performance at 80°C for 504 hours
Hardness change (Shore A)	ASTM D2240	Points	-2	-4
Volume change	ASTM D471	%	+3.1	+5.2
Tear strength	ASTM D412	MPa	8.94	7.54
Elongation at break	ASTM D412	%	269	237
2,Oil resistance 2.6 Resistance to 5W/30 engine oil (RME) at 80°C for 504 hours
Hardness change (Shore A)	ASTM D2240	Points	-1	-4
Volume change	ASTM D471	%	+3.52	+9.62
Tear strength	ASTM D412	MPa	9.05	7.24
Elongation at break	ASTM D412	%	215	189
3,Compression set at 150°C for 24 hours (the vulcanization condition of the sample 1^st curing at 175°C×10min and 2^nd curing at 230°C×16h)
Compression set	ASTM D395	%	26.48	23.48
4,Ozone resistance 80pphm×20% for elongation×40ºC×120 hours
Cracked or not	ASTM D1171	/	NO	NO
5,Low temperature retraction TR10
TR10	GB 7758	ºC	-20	-25

Our factory:

Our equipment:

Our certificates:

Dlivery & Shipment:

FAQ:

Q: Are you a factory or trading company?
A: We are rubber raw material manufacturer and owned 3 factories.

Q: Where is the loading port and How do you ship the goods?
A: Our factory is nearby Shanghai Port, but loading port can be negotiated. We could ship by sea, by air or by express(EMS, UPS, DHL, TNT, FEDEX and etc). Please confirm with us before placing orders.

Q: How can we guarantee the products' quality?
A: All the products must be tested refers to key specifications during the production and final inspection before shipment.

Q: What about the lead time?
A: It depends on the order quantity you place the order. Usually sample needs 5-8 working days, mass production needs 15-30 days.

Prev : Sinopec Thermoplastic Elastomer (hydrogenation styrene-butadiene block copolymer) S Next : Htv Silicone Rubber for Making Rubber Accessories Auto Parts Silicone Pads Sealants